- Print Technology
- SLA
- Characteristics
- High Accuracy, Fine Details, High Throughput
- Applications
- Fast Printing
- Ultimate Tensile Strength
- 52.0 MPa
- Notched Izod
- 26.0 J/m
- Elongation at Break
- 4.0 %
- Heat Deflection Temp. @ 1.8 MPa
- 57.0 °C
- Heat Deflection Temp. @ 0.45 MPa
- 74.0 °C
- Thermal Expansion
- 75.0 μm/m/°C
- Tensile Modulus
- 2300.0 MPa
- Flexural Modulus
- 2300.0 MPa
Draft Resin prints up to four times faster than Formlabs' General Purpose Resins on Form 3 Series printers, making it ideal for initial prototypes and rapid iterations to help bring products to market faster. Parts printed with Draft Resin exhibit a smooth grey finish and high accuracy.
Use 200-micron settings for fast print speeds, or use 100-micron settings for models with finer details.
Draft Resin is compatible with Form 3 and Form 2 Series printers. Choose Fast Model Resin on the Form 4 Series for three times faster print speed and improved mechanical properties.
- Print Technology
- SLA
- Characteristics
- High Accuracy, Fine Details, High Throughput
- Applications
- Fast Printing
- Ultimate Tensile Strength
- 52.0 MPa
- Notched Izod
- 26.0 J/m
- Elongation at Break
- 4.0 %
- Heat Deflection Temp. @ 1.8 MPa
- 57.0 °C
- Heat Deflection Temp. @ 0.45 MPa
- 74.0 °C
- Thermal Expansion
- 75.0 μm/m/°C
- Tensile Modulus
- 2300.0 MPa
- Flexural Modulus
- 2300.0 MPa
Select Printer Series and Resin Volume
Bulk Order Discount
- 15%
- 30 L
- 20%
- 60 L
- 25%
- 120 L
- 30%
- 240 L
- 35%
- 1,000 L
- 40%
- 2,000 L
- 45%
- 3,000 L
Compatibility
- 3D Printer
- Form 3, Form 3L, Form 3B, Form 3BL, Form 2
- Build Platform
- Form 3 Build Platform, Form 3 Build Platform 2, Form 3 Stainless Steel Build Platform, Form 3L Build Platform, Form 3L Build Platform 2L
- Tank
- Form 2 LT Tank, Form 3 Resin Tank V2.1, Form 3L Resin Tank V3
Draft Resin (Form 3)—
Why Choose Draft Resin
Bring products to market faster by leveraging Draft Resin early in the design process. Whether you are printing large parts or batches of smaller parts, Draft Resin ensures maximum print speed without compromising part quality.
Print Speed
Print up to 4x faster than standard resins
Part Quality
This reformulation reduced layer thickness by 33%, improving surface finish & accuracy
Professional Appearance
A new grey finish offers professional looking models
Ease of Use
This reformulation reduced support touchpoints and Form Wash and Form Cure times
Applications
Draft Resin prints up to 4 times faster than Formlabs Standard Resins, allowing you to iterate quickly and test multiple designs in a day.
Initial Prototypes
Rapid Design Iterations
High Throughput Parts
Material Properties
| Parameter |
Green |
Post-Cured at Room Temperature |
Post-Cured at 60 °C |
|---|---|---|---|
|
Ultimate Tensile Strength |
24 MPa |
36 MPa |
52 MPa |
|
Tensile Modulus |
0.8 GPa |
1.7 GPa |
2.3 GPa |
|
Elongation at Break |
14% |
5% |
4% |
|
Flexural Modulus |
0.6 GPa |
1.8 GPa |
2.3 GPa |
|
Notched Izod |
26 J/m |
29 J/m |
26 J/m |
Post-Processing
Washing
The foundational step in any SLA post-processing workflow is to remove any excess resin on the surface of the parts through an alcohol or ether wash.
SETTINGS
Curing
Post-curing for General Purpose Resins is optional. However, Formlabs recommends a short post-curing to reduce surface tack and improve mechanical properties.
SETTINGS
Form Cure V1 | Form Cure V2 | Form Cure L V1 | Form Cure L V2