- Print Technology
- SLA
- Colors
- Matte
- Characteristics
- High Accuracy, Fine Details
- Applications
- Fast Printing
- Tensile Modulus
- 2300.0 MPa
- Flexural Modulus
- 2200.0 MPa
- Ultimate Tensile Strength
- 48.0 MPa
- Elongation at Break
- 4.8 %
- Flexural Strength
- 85.0 MPa
- Notched Izod
- 23.0 J/m
- Unnotched Izod
- 324.0 J/m
- Heat Deflection Temp. @ 1.8 MPa
- 56.0 °C
- Heat Deflection Temp. @ 0.45 MPa
- 75.0 °C
- Thermal Expansion
- 76.0 μm/m/°C
Model Resin V3 is a fast-printing material for the production of high-accuracy models, such as miniatures, figurines, or restorative models in dentistry.
Model Resin V3 is compatible with Form 3 and Form 2 Series printers. Choose Precision Model Resin on the Form 4 Series for better accuracy, three times faster print speed, and improved aesthetics.
- Print Technology
- SLA
- Colors
- Matte
- Characteristics
- High Accuracy, Fine Details
- Applications
- Fast Printing
- Tensile Modulus
- 2300.0 MPa
- Flexural Modulus
- 2200.0 MPa
- Ultimate Tensile Strength
- 48.0 MPa
- Elongation at Break
- 4.8 %
- Flexural Strength
- 85.0 MPa
- Notched Izod
- 23.0 J/m
- Unnotched Izod
- 324.0 J/m
- Heat Deflection Temp. @ 1.8 MPa
- 56.0 °C
- Heat Deflection Temp. @ 0.45 MPa
- 75.0 °C
- Thermal Expansion
- 76.0 μm/m/°C
Select Printer Series and Resin Volume
Bulk Order Discount
- 15%
- 30 L
- 20%
- 60 L
- 25%
- 120 L
- 30%
- 240 L
- 35%
- 1,000 L
- 40%
- 2,000 L
- 45%
- 3,000 L
Compatibility
- 3D Printer
- Form 3, Form 3L, Form 3B, Form 3BL, Form 2
- Build Platform
- Form 3 Build Platform, Form 3 Build Platform 2, Form 3 Stainless Steel Build Platform, Form 3L Build Platform, Form 3L Build Platform 2L
- Tank
- Form 2 LT Tank, Form 3 Resin Tank V2.1, Form 3L Resin Tank V3
Model Resin V3 (Form 3)—
Why Choose Model Resin?
Model Resin enables dental professionals to print models in high volume, easily handle rush cases, and deliver highly-accurate custom fixed prosthetics and implants.
Fast
Produce models in high volume and easily handle rush cases.
Consistent and Reliable
Don’t spend time troubleshooting or redoing cases, get it right the first time.
Accurate
Deliver high-quality results with models you can rely on.
Applications
Formlabs 3D printers can quickly produce high-quality solid models, removable die models, and implant analog models with crisp margins and contacts.
Restorative models and implant analog models
Orthodontic models and diagnostic models
Material Properties*
| Parameter |
Value |
|---|---|
|
Ultimate Tensile Strength |
48 MPa |
|
Tensile Modulus |
2.3 GPa |
|
Elongation |
4.8% |
|
Flexural Modulus |
2.2 GPa |
|
Notched Izod |
24 J/m |
|
Heat Deflection Temperature @ 0.45 MPa |
75 ºC |
* Material properties may vary based on part geometry, print orientation, print settings, and temperature. Data for post-cured samples were measured on Type IV tensile bars printed on a Form 3 printer with 100 μm Model Resin settings, washed in a Form Wash for 10 minutes in ≥99% isopropyl alcohol, and post-cured at 60 °C for 5 minutes in a Form Cure.
Post-Processing
Washing
The foundational step in any SLA post-processing workflow is to remove any excess resin on the surface of the parts through an alcohol or ether wash.
SETTINGS
Curing
Post-curing for General Purpose Resins is optional. However, Formlabs recommends a short post-curing to reduce surface tack and improve mechanical properties.
SETTINGS
Form Cure V1 | Form Cure V2 | Form Cure L V1 | Form Cure L V2