- Print Technology
- SLA
- Characteristics
- Heat Resistant, High Strength, Fine Details, Ultra Stiff, Glass Filled
- Tensile Modulus
- 11000.0 MPa
- Flexural Modulus
- 9900.0 MPa
- Ultimate Tensile Strength
- 88.0 MPa
- Flexural Strength
- 158.0 MPa
- Notched Izod
- 20.0 J/m
- Unnotched Izod
- 130.0 J/m
- Elongation at Break
- 0.7 %
- Heat Deflection Temp. @ 1.8 MPa
- 92.0 °C
- Heat Deflection Temp. @ 0.45 MPa
- 238.0 °C
- Thermal Expansion
- 41.0 μm/m/°C
Rigid 10K Resin is a highly glass-filled and extremely stiff material that is similar to glass and fiber-filled thermoplastics. It prints with a smooth, matte, polished finish and is highly resistant to heat and chemicals.
Choose Rigid 10K Resin for precise industrial parts such as molds, jigs, dies, and other tooling for processes like injection molding, thermoforming, or blow molding, as well as functional prototypes and end-use parts requiring dimensional accuracy and stability under high temperatures and pressures.
- Print Technology
- SLA
- Characteristics
- Heat Resistant, High Strength, Fine Details, Ultra Stiff, Glass Filled
- Tensile Modulus
- 11000.0 MPa
- Flexural Modulus
- 9900.0 MPa
- Ultimate Tensile Strength
- 88.0 MPa
- Flexural Strength
- 158.0 MPa
- Notched Izod
- 20.0 J/m
- Unnotched Izod
- 130.0 J/m
- Elongation at Break
- 0.7 %
- Heat Deflection Temp. @ 1.8 MPa
- 92.0 °C
- Heat Deflection Temp. @ 0.45 MPa
- 238.0 °C
- Thermal Expansion
- 41.0 μm/m/°C
Select Printer Series and Resin Volume
Bulk Order Discount
- 15%
- 30 L
- 20%
- 60 L
- 25%
- 120 L
- 30%
- 240 L
- 35%
- 1,000 L
- 40%
- 2,000 L
- 45%
- 3,000 L
Compatibility
- 3D Printer
- Form 4L, Form 4BL, Form 4, Form 4B, Form 3, Form 3L, Form 3B, Form 3BL, Form 2
- Build Platform
- Form 4 Build Platform, Form 4 Flex Build Platform, Form 3 Build Platform, Form 3 Build Platform 2, Form 3 Stainless Steel Build Platform, Form 3L Build Platform, Form 3L Build Platform 2L, Form 4L Build Platform, Form 4L Flex Build Platform
- Tank
- Form 2 LT Tank, Form 3 Resin Tank V2.1, Form 3L Resin Tank V3, Form 4 Resin Tank, Form 4L Resin Tank
Rigid 10K Resin—
Why Choose Rigid 10K Resin?
Rigid 10K Resin is a high performance material that is strong, completely stiff, and stable.
Extremely Stiff
Resistant to deformation under a variety of forces, pressures, and torques.
High Thermal and Chemical Resistance
Withstands high temperatures and a variety of chemicals.
Precise
Produce strong, detailed, and accurate molds or models.
Incredible Surface Quality
Exhibits a smooth matte finish.
Applications
Rigid 10K Resin is ideal for creating rigid, strong, industrial-grade prototypes. Rigid 10K Resin can be faster and easier to print compared to milling aluminum and steel.
Short-run injection mold masters and inserts
Heat resistant and fluid exposed components, jigs, and fixtures
Aerodynamic test models
Prototypes that simulate the stiffness of glass and fiber-filled thermoplastics
Prototype molds for blow molding
Molds for thermoforming
Material Properties*
| Parameter | Rigid 10K Resin |
|---|---|
|
Ultimate Tensile Strength |
88 MPa |
|
Tensile Modulus |
11 GPa |
|
Elongation |
1.7% |
|
Flexural Modulus |
9.9 GPa |
|
Notched Izod |
20 J/m |
|
Heat Deflection Temp @ 0.45 MPa |
238 °C |
|
Thermal Expansion, 0-150 °C |
41 μm/m/°C |
* Data was obtained from parts printed Form 3, 100 µm and post-cured with a Form Cure for 60 minutes at 70°C.
Post-Processing
Washing
The foundational step in any SLA post-processing workflow is to remove any excess resin on the surface of the parts through an alcohol or ether wash.
SETTINGS
Curing
Post-curing Engineering and Specialty Resins is essential for parts to achieve their full strength and functionality. This step completes the chemical reaction initiated during printing, transforming the part from its green state into a fully finished component.
SETTINGS
Form Cure V1 | Form Cure V2 | Form Cure L V1 | Form Cure L V2
Request a Free Rigid 10K Resin Sample Part
See and feel Formlabs quality firsthand. We’ll ship a free Rigid 10K Resin 3D printed sample part to your office.