Dental LT Clear Resin
- Print Technology
- SLA
- Colors
- Transparent
- Categories
- Dental
- Applications
- Dental
- Ultimate Tensile Strength
- 52.0 MPa
- Flexural Modulus
- 2300.0 MPa
- Elongation at Break
- 12.0 %
- Flexural Strength
- 84.0 MPa
- Shore Hardness
- 78.0 D
- Notched Izod
- 449.0 J/m
- Tensile Modulus
- 2080.0 MPa
Dental LT Clear Resin V2 is a long-term biocompatible material for directly printing affordable, high-quality hard splints and occlusal guards in-house. Highly durable and resistant to fracture, this color-corrected material prints clear, polishes to high optical transparency, and resists discoloration over time.
Read our application guide to learn the complete workflow and best practices for making 3D printed splints and night guards on your Formlabs 3D printer.
Regional Availability
Product availability is limited to certain regions. See regional availability.
- Print Technology
- SLA
- Colors
- Transparent
- Categories
- Dental
- Applications
- Dental
- Ultimate Tensile Strength
- 52.0 MPa
- Flexural Modulus
- 2300.0 MPa
- Elongation at Break
- 12.0 %
- Flexural Strength
- 84.0 MPa
- Shore Hardness
- 78.0 D
- Notched Izod
- 449.0 J/m
- Tensile Modulus
- 2080.0 MPa
Select Printer Series and Resin Volume
Bulk Order Discount
- 15%
- 30 L
- 20%
- 60 L
- 25%
- 120 L
- 30%
- 240 L
- 35%
- 1,000 L
- 40%
- 2,000 L
- 45%
- 3,000 L
Compatibility
- Compatible Build Platform
- Form 4 Build Platform, Form 4 Flex Build Platform, Form 3 Build Platform, Form 3 Build Platform 2, Form 3 Stainless Steel Build Platform, Form 3L Build Platform, Form 3L Build Platform 2L, Form 4L Build Platform, Form 4L Flex Build Platform
- Compatible Tank
- Form 4 Resin Tank, Form 4L Resin Tank, Form 2 LT Tank, Form 3 Resin Tank V2.1, Form 3L Resin Tank V3
- Compatible Printer
- Form 4B, Form 4BL, Form 3B, Form 3BL, Form 2
Dental LT Clear Resin—
Why Choose Dental LT Clear Resin V2?
Dental LT Clear Resin V2 provides dental professionals with a durable, color-corrected material for the convenient production of long-lasting and hard occlusal splints.
High Performance
Provide fracture-resistant, durable and long-lasting bite splints to patients.
Aesthetic
Polish splints to high optical transparency, aiding in patient acceptance.
Accurate and Consistent
Run a lean and profitable workflow with consistent production of aligners.
Biocompatibility
Provide the patient and clinician the peace of mind they deserve.
Applications
Dental LT Clear Resin V2 is Formlabs’ second-generation, long-term biocompatible material for clear splints, night guards, and occlusal guards.
Splints
Occlusal Guards and Night Guards
Material Properties*
Dental LT Clear Resin (V2)
| Parameter | Value |
|---|---|
|
Ultimate Tensile Strength |
52 MPa |
|
Tensile Modulus |
2080 MPa |
| Elongation |
12% |
|
Flexural Modulus |
2300 MPa |
|
Impact Strength (Unnotched IZOD) |
449 J/m |
|
Shore Hardness |
78 D |
* Material properties may vary based on part geometry, print orientation, print settings, and temperature. Data were measured on post-cured samples printed on a Form 3B printer with 100 µm Dental LT Clear Resin V2 settings, washed in a Form Wash for 20 minutes in 99% isopropyl alcohol, and post-cured at 60 °C for 60 minutes in a Form Cure.
Post-Processing
Form Wash Settings
Duration
20 min in IPA
Notes
To ensure that finished parts are biocompatible, follow all part washing notes in the Instructions for Use. Maintain separate wash buckets for biocompatible materials. Wash for 15 minutes, then remove parts and soak in fresh IPA for 5 minutes. Do not leave Dental LT Clear Resin in IPA for longer than 20 minutes total, as excessive solvent exposure affects the quality of the final part.
Form Cure Settings
Duration
60 min
Temperature
60 °C
Notes
Post-curing as recommended in the material-specific Instructions for Use is required to ensure optimal performance and biocompatibility of 3D printed dental appliances.