Flexible 80A Resin

Engineering

Application

SLA

Translucent

8.9 MPa

Ultimate Tensile Strength

120.0%

Elongation at Break

80.0 A

Shore Hardness

Printer

Form 2, Form 3, Form 3+, Form 3B, Form 3B+, Form 3L, Form 3BL, Form 4, Form 4B, Form 4L, Form 4BL

Resin Tank

Form 2 LT Tank, Form 3 Resin Tank V2.1, Form 3L Resin Tank V3, Form 4 Resin Tank, Form 4L Resin Tank

Build Platform

Form 4 Build Platform, Form 4 Build Platform Flex, Form 3 Build Platform, Form 3 Build Platform 2, Form 3 Stainless Steel Build Platform, Form 3L Build Platform, Form 4L Build Platform L

Flexible 80A Resin

$199

excluding VAT

RS-CFG-FL80-01
$199

excluding VAT

Select Printer Series and Resin Volume

Resin Discount
Bulk order quantity (L)Discount %
10%
3015%
6020%
12025%
24030%
1,00035%
2,00040%
3,00045%+
Flexible 80A Resin a stiff, soft-touch, translucent elastomer with an 80A Shore durometer that is ideal for prototyping rubber-like parts with the flexibility of harder rubber or TPU.

Parts printed in Flexible 80A Resin can withstand bending, flexing, and compression, even through repeated cycles.
Hand produced in Flexible 80A Resin

Why Choose Flexible 80A Resin?

Create silicone, urethane and rubber-like parts. Produce flexible parts in-house in a matter of hours, replacing outsourcing and molding.


Elastomeric

Leverage bendable parts that return to shape slowly.


Soft and Strong

Stretch and compress parts through repeated cycles without cracking.


Transparent

Create objects that are clear, providing visibility into the model.


Durable

Support user testing with looks and feels like prototypes that can be put to the test.

Applications

Flexible 80A Resin is ideal for hard, flexible prototypes and a great alternative to mold making.

Consider Flexible 80A Resin for:

Handles, grips, and overmolds
Seals, gaskets, and masks
Cushioning, damping, and shock absorption
Cartilage, tendon, and ligament anatomy

Material Properties*

Flex 80A Resin

Ultimate Tensile Strength

7.2 MPa

Stress at 50% Elongation

2.6 MPa

Stress at 100% Elongation

4.5 MPa

Elongation

135%

Tear Strength

22 kN/m

Hardness Shore A

80A
Download the Flexible 80A Resin Technical Data Sheet

Material properties may vary based on part geometry, print orientation, print settings, and temperature. Data was obtained from parts printed on a Form 3 with 100 µm Flexible 80A settings, washed in a Form Wash for 10 minutes, and post-cured at 60°C for 10 minutes in a Form Cure.

Post-Processing

Form Wash Settings

Duration

10 minutes + 10 minutes

Notes

Wash parts printed in Flexible 80A Resin in two cycles, preferably using fresh solvent for the second wash. When washed in TPM, Flexible 80A Resin remains waxy when printed at any layer thickness and requires post-cure. Post-curing removes the waxiness.

Form Cure Settings

Duration

10 min

 

Temperature

60 °C

Notes

For parts printed in an engineering-focused resin (such as those in the Rigid, Tough & Durable, and Flexible & Elastic families), post-curing ensures that the parts reach their optimal mechanical properties and can function as designed. There is only one recommended post-curing time for Flexible 80A Resin.