Black Resin 1 L
3D print strong, precise concept models and prototypes that bring your ideas to life with Formlabs’ library of Standard Resins. With a matte surface finish, opaque appearance, and precise details, prints are ready to use right off the printer. Their neutral undertone makes a great base for parts that will eventually be painted or undergo other finishing processes.
Black Resin is formulated for models with very small features and intricate details.
Supports print resolutions: 100, 50, and 25 microns.
- Black Resin 1 L
Why Choose Black Resin?
Leverage Black Resin to iterate on high-resolution prototypes and models that capture astonishing detail without sacrificing strength.
Produce prints with smooth, opaque surfaces ideal for model making and looks-like prototyping, rivaling injection-molded plastics.
Deliver delicate features and fine details.
Ease of Use
Start using your parts quickly, as Formlabs’ Standard Resins only need minimal post-processing.
Paint or use other finishing processes to elevate your model or prototype.
Black Resin supports high detail with a smooth, matte surface finish with great mechanical properties.
Consider Black Resin for:
Ultimate Tensile Strength
Heat Deflection Temp @ 0.45 MPa
* Material properties may vary based on part geometry, print orientation, print settings, and temperature. Data was obtained from parts printed using Form 2, 100 μm, Clear settings and post-cured with 1.25 mW/cm³ of 405 nm LED light for 60 minutes at 60°C.
Form Wash Settings
10 min in IPA
When using a single wash bucket, residue from previously washed parts deposits on part surfaces. If washing darker-colored materials like Black Resin in the same wash bucket as lighter-colored materials like White Resin or Clear Resin, some color transfer may occur.
Form Cure Settings
All standard opaque Formlabs resins (including Grey, Black, White, Color, and Model Resin) have equivalent mechanical properties. While the recommended post-cure time is 30 minutes, post-curing for 60 minutes will result in a small additional gain in tensile modulus. This post-cure setting can be used with any of these resins.