Fast Model Resin

General Purpose, Engineering

Application

SLA

Post-Curing Optional

62 MPa

Ultimate Tensile Strength

2.67 GPa

Tensile Modulus

11 %

Elongation at Break

Printer

Form 4, Form 4B, Form 4L, Form 4BL

Resin Tank

Form 4 Resin Tank, Form 4L Resin Tank

Build Platform

Form 4 Build Platform, Form 4 Flex Build Platform, Form 4L Build Platform, Form 4L Flex Build Platform

Fast Model Resin
Estimated delivery: Sep 5 - 15

Select Printer Series and Resin Volume

Resin Discount
Contact Sales
Bulk order quantity (L)Discount %
10%
3015%
6020%
12025%
24030%
1,00035%
2,00040%
3,00045%
Fast Model Resin is Formlabs’ fastest resin, capable of printing at speeds of over 100 mm per hour. Print dental models in minutes or large prototypes in less than two hours.

Fast Model Resin is the next generation of Draft Resin that leverages the Form 4 Series to print three times faster, while offering improved mechanical properties.
3D printed parts in Fast Model Resin

Why Choose Fast Model Resin?

Fast Model Resin is Formlabs’ fastest 3D printing resin, capable of printing at speeds of 100 mm per hour.


Parts As Fast As You Can Design Them

Print a fully packed build on Form 4 in 2 hours.


Fast Post-Processing

Post-process parts quickly with a 5-minute wash and 5-minute room temperature post-cure.


Presentation-Ready Appearance

Create parts with a matte grey color and smooth surface finish.


Extremely Low-Odor Printing

Print with ultra-low volatile organic compounds (VOCs) for a pleasant and comfortable user experience.

Applications for Fast Model Resin

Fast Model Resin is capable of 3D printing a full Form 4 build volume in under two hours, making it ideal for rapid prototyping and high-throughput applications.

Consider Fast Model Resin for:

Initial prototypes for shape and feel
Rapid design iterations
Large models that can print quickly
Dental models for thermoforming aligners
Parts 3D printed with Fast Model Resin

What’s New With Fast Model Resin?

Fast Model Resin is the next generation of Draft Resin, formulated to leverage the new Form 4 ecosystem. Compared to Draft Resin V2, Fast Model Resin is:

Faster — formulated to take advantage of the new Form 4 ecosystem to print three times faster
Stronger and stiffer — 45% higher strength and modulus
More opaque and matte in color

Mechanical Properties

Post-cured at room temperature for 5 minutes

Ultimate Tensile Strength

55 MPa

Tensile Modulus

2500 MPa

Elongation at Break

15%

Flexural Strength

98 MPa

Flexural Modulus

2600 MPa

Notched Izod

30 J/m

Heat Deflection Temperature at 0.45 MPa

58 °C

Post-cured at 60 °C for 15 minutes

Ultimate Tensile Strength

62 MPa

Tensile Modulus

2700 MPa

Elongation at Break

11%

Flexural Strength

106 MPa

Flexural Modulus

2700 MPa

Notched Izod

37 J/m

Heat Deflection Temperature at 0.45 MPa

76 °C

Post-Processing

Wash Settings

Duration

5 minutes

Notes

Start with a 5-minute wash and modify the wash time based on your part geometry and solvent purity.

Form Cure Settings

Default

5 minutes at room temperature

Enhanced

15 minutes at 60 °C

Notes

Post-curing is optional for parts printed in Fast Model Resin. However, we recommend either a 5-minute room temperature cure to reduce surface tack and improve mechanical properties, or a 15-minute cure at 60 °C for the highest strength, stiffness, and heat deflection temperature.