Why Choose Castable Wax Resin?
With high strength and stiffness, Castable Wax Resin makes it possible to print ultrafine and thin structures.
Clean, Reliable Casting
Contains 20% wax with zero ash content and clean burnout.
Faster and Simpler Workflow
Printed parts are strong enough to handle with no post-cure required, meaning they are ready to use right away.
Smooth, Refined Surfaces
Easily remove light-touch support tips that don’t leave dimples in your parts.
High Green Strength
Ensure shape retention for thin patterns such as wire filigree.
Applications
Castable Wax Resin is ideal for lightweight, intricate jewelry or for prototypes and production. For Dental, this material is ideal for crowns, bridges, removable partial denture frameworks, and patterns for casting and pressing.
Consider Castable Wax Resin for:
Material Properties*
Castable Wax Resin does not require post-curing. Allow parts to fully dry before casting.*
Castable Wax Resin
Ultimate Tensile Strength
Tensile Modulus
Elongation
Temp @ 5% Mass Loss
Ash Content (TGA)
* Material properties may vary based on part geometry, print orientation, print settings, and temperature.
** Data was optained from green parts, printed using Form 2, Castable 50 μm Fine Detail settings and washed without post-cure.
Post-Processing
Form Wash Settings
5 min in IPA
Wash Castable parts for the shortest time necessary to remove liquid resin. Ensure that all solvent has evaporated or been removed from the parts before curing and casting.
Form Cure Settings
N/A min
N/A °C
Castable Wax Resin does not require post-curing. Allow parts to fully dry before casting. While post-curing Castable Wax parts should not affect castability, post-curing may shrink parts slightly (by less than 1%), which can cause distortion.