Rigid 4000 Resin
Engineering
Application
SLA
High Strength
69.0 MPa
Ultimate Tensile Strength
4.1 GPa
Tensile Modulus
105.0 MPa
Flexural Strength
Printer
Form 2, Form 3, Form 3+, Form 3B, Form 3B+, Form 3L, Form 3BL, Form 4, Form 4B, Form 4L, Form 4BL
Resin Tank
Form 2 LT Tank, Form 3 Resin Tank V2.1, Form 3L Resin Tank V3, Form 4 Resin Tank, Form 4L Resin Tank
Build Platform
Form 4 Build Platform, Form 4 Build Platform Flex, Form 3 Build Platform, Form 3 Build Platform 2, Form 3 Stainless Steel Build Platform, Form 3L Build Platform, Form 3L Build Platform 2L, Form 4L Build Platform L
Rigid 4000 Resin
Select Printer Series and Resin Volume
Bulk order quantity (L) | Discount % |
---|---|
1 | 0% |
30 | 15% |
60 | 20% |
120 | 25% |
240 | 30% |
1,000 | 35% |
2,000 | 40% |
3,000 | 45%+ |
Choose Rigid 4000 Resin for stiff and strong engineering-grade prototypes, general load-bearing applications, and industrial parts that need to withstand significant load without bending.
Printer compatibility: Form 2, Form 3, Form 3+, Form 3B, Form 3B+, Form 3L, Form 3BL, Form 4, Form 4B, Form 4L, Form 4BL
Compatible with these resin tanks: Form 2 LT Tank, Form 3 Resin Tank V2.1, Form 3L Resin Tank V3, Form 4 Resin Tank, Form 4L Resin Tank
Compatible with these build platforms: Form 4 Build Platform, Form 4 Build Platform Flex, Form 3 Build Platform, Form 3 Build Platform 2, Form 3 Stainless Steel Build Platform, Form 3L Build Platform, Form 3L Build Platform 2L, Form 4L Build Platform L
Why Choose Rigid 4000 Resin?
Rigid 4000 Resin is a glass-filled material that has the highest tensile strength in our Engineering Resin Library.
Stiff
Resistant to deformation under a variety of forces, pressures, and torques.
High Thermal and Chemical Resistance
Withstands high temperatures and a variety of chemicals.
Precise
Produce strong, detailed, and accurate molds or models.
Smooth, Matte Finish
Deliver parts that look and feel like a finished product.
Applications
Produce stiff and strong engineering-grade prototypes that can be load-bearing.
Consider Rigid 4000 Resin for:
Material Properties*
Rigid 4000 Resin
Ultimate Tensile Strength
Tensile Modulus
Elongation
Flexural Modulus
Notched Izod
Heat Deflection Temp. @ 0.45 MPa
Thermal Expansion (0-150 °C)
* Material properties can vary with part geometry, print orientation, print settings, and temperature. Data was obtained from parts printed using Form 3, 100 μm, Rigid settings and post-cured with a Form Cure for 15 minutes at 80 °C.
Post-Processing
Form Wash Settings
15 minutes in IPA
Rigid 4000 Resin contains glass particles, which strengthens printed parts. Maintain separate wash buckets to prevent glass particles adhering to parts printed with other resins.
Form Cure Settings
15 min
80 °C
For parts printed in an engineering-focused resin (such as those in the Rigid, Tough & Durable, and Flexible & Elastic families), post-curing ensures that the parts reach their optimal mechanical properties and can function as designed. There is only one recommended post-curing time for Rigid 4000 Resin V1.