Tough 2000 Resin
Engineering
Application
SLA
Stiff & Strong
91 μm/m/°C
Thermal Expansion
46 MPa
Ultimate Tensile Strength
2.2 GPa
Tensile Modulus
Printer
Form 2, Form 3, Form 3+, Form 3B, Form 3B+, Form 3L, Form 3BL, Form 4, Form 4B, Form 4L, Form 4BL
Resin Tank
Form 2 LT Tank, Form 3 Resin Tank V2.1, Form 3L Resin Tank V3, Form 4 Resin Tank, Form 4L Resin Tank
Build Platform
Form 4 Build Platform, Form 4 Flex Build Platform, Form 3 Build Platform, Form 3 Build Platform 2, Form 3 Stainless Steel Build Platform, Form 3L Build Platform, Form 3L Build Platform 2L, Form 4L Build Platform, Form 4L Flex Build Platform
Select Printer Series and Resin Volume
| Bulk order quantity (L) | Discount % |
|---|---|
| 1 | 0% |
| 30 | 15% |
| 60 | 20% |
| 120 | 25% |
| 240 | 30% |
| 1,000 | 35% |
| 2,000 | 40% |
| 3,000 | 45%+ |
Choose Tough 2000 Resin for prototyping strong and sturdy parts that should not bend easily, as well as jigs and fixtures requiring minimal deflection.
Printer compatibility: Form 2, Form 3, Form 3+, Form 3B, Form 3B+, Form 3L, Form 3BL, Form 4, Form 4B, Form 4L, Form 4BL
Compatible with these resin tanks: Form 2 LT Tank, Form 3 Resin Tank V2.1, Form 3L Resin Tank V3, Form 4 Resin Tank, Form 4L Resin Tank
Compatible with these build platforms: Form 4 Build Platform, Form 4 Flex Build Platform, Form 3 Build Platform, Form 3 Build Platform 2, Form 3 Stainless Steel Build Platform, Form 3L Build Platform, Form 3L Build Platform 2L, Form 4L Build Platform, Form 4L Flex Build Platform
Tough 2000 Resin has been added to your cart.
Why Choose Tough 2000 Resin?
Tough 2000 Resin is a functional material that’s difficult to bend and will hold up with extended use.
Stiff and Sturdy
Produce strong parts with minimal deformation.
Resistant
Withstand intermittent or constant loads required of heavy-duty parts.
Aesthetic, Neutral Color
Create professional-looking parts that blend seamlessly into their environment.
Robust
Iterate with higher confidence and reduce brittle failures.
Applications
Tough 2000 Resin is ideal for rugged prototyping or simulating the strength and stiffness of ABS.
Consider Tough 2000 Resin for:
Material Properties*
Tough 2000 Resin
Ultimate Tensile Strength
Tensile Modulus
Elongation
Flexural Modulus
Notched Izod
Heat Deflection Temp @ 0.45 MPa
* Material properties may vary based on part geometry, print orientation, print settings, and temperature. Data was obtained from parts printed using Form 2, 100 μm, Tough 2000 settings and post-cured with a Form Cure for 120 minutes at 80 °C.
Post-Processing
Form Wash Settings
10 minutes + 10 minutes in IPA
Part surfaces may become tacky if washed in IPA with more than 5% resin concentration. Use fresh solvent if your parts remain tacky after washing. Parts with two wash times require two wash cycles. For the second wash cycle, use clean solvent. The first wash cycle removes the bulk of the resin, while the second cycle fully cleans the parts.
Form Cure Settings
60 min
70 °C
For parts printed in an engineering-focused resin (such as those in the Rigid, Tough & Durable, and Flexible & Elastic families), post-curing ensures that the parts reach their optimal mechanical properties and can function as designed. There is only one recommended post-curing time for Tough 2000 Resin.