Why Choose White Resin?

Leverage White Resin to iterate on high-resolution prototypes and models that capture astonishing detail without sacrificing strength.


Opaque and Matte

Produce prints with smooth, opaque surfaces ideal for model making, painting, and looks-like prototyping.


High Part Quality

Show off fine details and iterate on designs when you want to focus on form alone.


Ease of Use

Start using your parts quickly, as Formlabs’ Standard Resins only need minimal post-processing.


Neutral Undertone

Paint or use other finishing processes to elevate your model or prototype.

Applications

White Resin supports high detail with a smooth, matte surface finish with great mechanical properties.

Consider White Resin for:

General purpose prototyping and design
Models with very small features and intricate details
Base for painted prints
Presentation-ready pieces

Material Properties*

White Resin

Ultimate Tensile Strength

65 MPa

Tensile Modulus

2.6 GPa

Elongation

6%

Flexural Modulus

2.2 GPa

Notched Izod

25 J/m

Heat Deflection Temp @ 0.45 MPa

73 ºC

Material properties may vary based on part geometry, print orientation, print settings, and temperature. Data was obtained from parts printed using Form 2, 100 μm, Clear settings and post-cured with 1.25 mW/cm³ of 405 nm LED light for 60 minutes at 60°C.

Post-Processing

Form Wash Settings

Duration

10 min in IPA

Notes

When using a single wash bucket, residue from previously washed parts deposits on part surfaces. If washing darker-colored materials like Black Resin in the same wash bucket as lighter-colored materials like White Resin or Clear Resin, some color transfer may occur.

Form Cure Settings

Duration

30 min

 

Temperature

60 °C

Notes

All standard opaque Formlabs resins (including Grey, Black, White, Color, and Model Resin) have equivalent mechanical properties. While the recommended post-cure time is 30 minutes, post-curing for 60 minutes will result in a small additional gain in tensile modulus. This post-cure setting can be used with any of these resins.