High Temp Resin

Engineering

Application

SLA

Translucent

2.8 GPa

Tensile Modulus

238.0 °C

Heat Deflection Temp. @ 0.45 MPa

49.0 MPa

Ultimate Tensile Strength

Printer

Form 2, Form 3, Form 3+, Form 3B, Form 3B+, Form 3L, Form 3BL, Form 4, Form 4B, Form 4L, Form 4BL

Resin Tank

Form 2 Resin Tank (PDMS), Form 2 LT Tank, Form 3 Resin Tank V2.1, Form 3L Resin Tank V3, Form 4 Resin Tank, Form 4L Resin Tank

Build Platform

Form 4 Build Platform, Form 4 Build Platform Flex, Form 3 Build Platform, Form 3 Build Platform 2, Form 3 Stainless Steel Build Platform, Form 3L Build Platform, Form 3L Build Platform 2L, Form 4L Build Platform L

High Temp Resin

$199
RS-CFG-HTAM-02
Estimated delivery: Apr 1 - 7
$199

Select Printer Series and Resin Volume

Resin Discount
Bulk order quantity (L)Discount %
10%
3015%
6020%
12025%
24030%
1,00035%
2,00040%
3,00045%+
High Temp Resin has a heat deflection temperature (HDT) of 238 °C @ 0.45 MPa — the highest among Formlabs resins.

Choose High Temp Resin to print detailed, precise prototypes and end use parts that require high thermal stability, such as molds and inserts, parts exposed to hot air, gas, and fluid flow, as well as heat-resistant mounts, housings, and fixtures.

Form 4(B)L print settings are in progress, view the settings roadmap to see when settings for this material will be available on the Form 4(B)L.

High Temp Resin

Why Choose High Temp Resin

Our best material for stability under heat, High Temp Resin offers the highest heat deflection temperature among Formlabs resins.


High Thermal Stability

High Temp Resin offers the highest heat deflection temperature of any Formlabs material.


Ease of Use

Formlabs' accessible technology makes it easy to experiment with high temperature applications.

Applications

With the highest Heat Deflection Temperature of any Formlabs material, High Temp Resin is ideal for applications that require resistance to high temperatures.

Hot air, gas, and fluid flow
Heat resistant mounts, housings, and fixtures
Molds and inserts

Material Properties

Download High Temp Resin Technical Data Sheet
Green
Post-Cured at 60°C
Ultimate Tensile Strength
21 MPa
58 MPa
Tensile Modulus
0.75 GPa
2.8 GPa
Elongation at Break
14%
3.3%
Flexural Modulus
0.7 GPa
2.6 GPa
Notched Izod
33 J/m
18 J/m

Post-Processing

Form Wash Settings

Duration

6 min

 

Notes

Do not leave High Temp Resin in solvent for longer than 6 minutes total, as excessive solvent exposure affects the quality of the final part.

Form Cure Settings

Duration

120 min

 

Temperature

80 °C

Notes

There are several post-curing options for High Temp V2. Refer to the technical data sheet to understand how different options affect mechanical properties, and choose the post-cure option that is best suited to the intended application. To achieve the highest HDT of 238 °C @ 0.45 MPa: (1) Post-cure parts in Form Cure for 120 min at 80 °C. (2) Thermally post-cure parts in a non-food oven for 3 hours at 160 °C. For applications that do not require the maximum heat resistance, post-cure parts in Form Cure for 60 min at 60 °C.